PHÂN HỦY PHẨM ĐỎ ĐH 120 TRONG MÔI TRƯỜNG NƯỚC BẰNG QUÁ TRÌNH NỘI ĐIỆN PHÂN TRÊN VẬT LIỆU NANO Fe/GrO

Abstract

Successfully fabricated nanomaterials Fe/GrO by depositing Fe particles on the surface of GrO materials using NaBH₄ and FeSO₄. Materials Fe/GrO is used removal of red dye ĐH 120 from aqueous solution by internal microelectrolysis. The results show that with optimal conditions for red dye ĐH 120 decomposition is pH of 2, contact time of 150 minutes, material weight of 1.67 g/L, shaking rate of 300 revolutions per minute (rpm), red dye ĐH 120 removal efficiency is 61.18%, with the initial concentration is 200 mg/L. The process of decomposition of red dye ĐH 120 by Fe/GrO material follows the apparent first-order kinetic model, with reaction rate constant k =  0.0118 min^-1. The results show that materials Fe/GrO can be applied to remove red dye ĐH 120 from aqueous solution by internal microelectrolysis before biological treatment.

Tóm tắt

Chế tạo thành công vật liệu nano Fe/GrO bằng cách đưa các hạt Fe chế tạo từ NaBH₄ và FeSO₄ lên bề mặt GrO. Vật liệu nano Fe/GrO được dùng phân hủy phẩm nhuộm đỏ ĐH 120 trong dung dịch nước bằng phương pháp nội điện phân. Kết quả cho thấy điều kiện tối ưu để thuốc nhuộm đỏ ĐH 120 phân hủy là pH = 2, thời gian tiếp xúc 150 phút, khối lượng nguyên liệu 1,67 g/L, tốc độ lắc 300 vòng/phút, hiệu suất khử thuốc nhuộm đỏ ĐH 120 là 61,18%, với nồng độ ban đầu là 200 mg/L. Quá trình phân hủy thuốc nhuộm đỏ ĐH 120 bằng vật liệu nano Fe/GrO tuân theo mô hình động học biểu kiến bậc nhất, với hằng số tốc độ phản ứng k = 0,0118 phút^-1. Kết quả cho thấy vật liệu nano Fe/GrO có thể dùng để phân hủy thuốc nhuộm đỏ ĐH 120 trong dung dịch nước bằng phương pháp nội điện phân trước khi xử lý bằng phương pháp sinh học.