NGHIÊN CỨU ĐỀ XUẤT THÔNG SỐ CÔNG NGHỆ TẠO VÁN LVL TỪ TỔ HỢP VÁN BÓC GỖ KEO TAI TƯỢNG, BẠCH ĐÀN URO, MỠ, THÔNG CARIBÊ ĐỂ SẢN XUẤT GỖ KHỐI

Abstract

This study investigated the suitable technological parameters to produce LVL from Acacia mangium Willd., Eucalyptus urophylla, Manglietia conifera Dandy and Pinus Caribaea Morelet veneer as material of multilaminar wood. For each pair of Acacia mangium Willd. (K) - Manglietia conifera Dandy (M), Eucalyptus urophylla (BD) - Manglietia conifera Dandy (M) and Pinus caribaea Morelet (T) - Eucalyptus urophylla (BD), the appropriate layered structure was: structure 1 (K-M-K-M-K-M-K-M-K-M-K-M-K-M), structure 3 (M-M-BD-BD-M-M-BD-M-BD-BD-M-M-BD-BD) and structure 1 (T-BD-T-BD-T-BD-T-BD-T-BD-T-BD-T-BD) respectively. The spread rate of 180 g/m2 and hot pressure of 1.2 MPa were chosen for the pair of Pinus caribaea Morelet - Eucalyptus urophylla and the spread rate of 160 g/m2 and hot pressure of 1.2 MPa were chosen for the other two pairs because these make LVL product with the most suitable adhesion quality and mechanical properties.

Tóm tắt

Nghiên cứu này đã xác định được thông số công nghệ (cấu trúc xếp lớp, lượng keo tráng và chế độ ép) tạo ván LVL (Laminated veneer lumber) từ ván bóc của các loài cây Keo tai tượng (Acacia mangium Willd.), Bạch đàn Uro (Eucalyptus urophylla), Mỡ (Manglietia conifera Dandy) và Thông Caribê (Pinus caribaea Morelet) làm nguyên liệu cho gỗ khối. Đối với từng cặp gỗ Keo tai tượng (K) - Mỡ (M), Bạch đàn Uro (BĐ) - Mỡ (M) và Thông Caribê (T) - Bạch đàn Uro (BĐ), cấu trúc xếp lớp phù hợp đã được lựa chọn lần lượt là: cấu trúc 1 (K-M-K-M-K-M-K-M-K-M-K-M-K-M), cấu trúc 3 (M-M-BĐ-BĐ-M-M-BĐ-M-BĐ-BĐ-M-M-BĐ-BĐ) và cấu trúc 1 (T-BĐ-T-BĐ-T-BĐ-T-BĐ-T-BĐ-T-BĐ-T-BĐ). Lượng keo tráng 180 g/m², áp lực ép 1,2 MPa đối với cặp gỗ Thông Caribê - Bạch đàn Uro và lượng keo tráng 160 g/m², áp lực ép 1,2 MPa đối với 2 cặp gỗ còn lại cho chất lượng dán dính và tính chất cơ học phù hợp nhất nên được lựa chọn để tạo ván LVL.