KHẢO SÁT KHẢ NĂNG KHÁNG VI KHUẨN RALSTONIA SOLANACEARUM GÂY BỆNH HÉO XANH Ở THỰC VẬT BẰNG NANO BẠC

Abstract

Silver nanoparticles have been researched and proved to have high antibacterial properties and have been used to treat diseases in medicine. This study was performed with three treatments for silver nanoparticles which were reduced in extracts of three plants: Ageratum conyzoides, Fortunella japonica and Ocimum tenuiflorum for the purpose of investigating the antibacterial resistance to Ralstonia solanacearum – bacterium causing a fusarium wilt disease. With the disk agar diffusion and the spectroscopic measurement method, study was investigated at 4 concentrations of 20, 40, 60 and 80 ppm silver nano. All three treatments showed the ability to inhibit the growth of 3 strains of Ralstonia solanacearum RS5, RS7, RS9, with the highest antibacterial zone value at the concentration of 80 ppm in the treatments Ageratum conyzoides, Fortunella japonica, Ocimum tenuiflorum ranged respectively from 7 to 11.3 mm, from 7 to 12.6 mm and from 4.3 to 4.6 mm. 

Tóm tắt

Vật liệu nano bạc đã được nghiên cứu và công bố là có tính kháng khuẩn cao và đã được ứng dụng để điều trị bệnh trong y học. Nghiên cứu được thực hiện với ba nghiệm thức nano bạc được khử trong dịch chiết từ ba loại thực vật là Ngũ Sắc, Kim Quýt, Hương Nhu nhằm mục đích khảo sát khả năng kháng vi khuẩn Ralstonia solanacearum – một loài vi khuẩn gây bệnh héo xanh ở thực vật. Với phương pháp khoanh giấy thấm và đo quang phổ tại 4 nồng độ nano bạc 20, 40, 60, 80 ppm cả ba nghiệm thức đều cho khả năng ức chế sự phát triển của 3 dòng vi khuẩn Ralstonia solanacearum RS5, RS7, RS9 với giá trị đường kính vòng vô khuẩn (ĐKVVK) cao nhất ở nồng độ 80 ppm lần lượt ở các nghiệm thức là Ngũ Sắc: ĐKVVK dao động từ 7 – 11,3 mm; Kim Quýt: ĐKVVK dao động từ 7 – 12,6 mm; Hương Nhu: ĐKVVK dao động từ 4,3 – 4,6 mm.