NGHIÊN CỨU XÂY DỰNG QUY TRÌNH CÔNG NGHỆ TẠO VÁN LẠNG DỌC GỖ TẾCH

Abstract

Analyze, select and propose a technological process for Teak longthwise wood veneer slicer products with a thickness of 1 mm, 2 mm, 3 mm as follow: Selecting raw materials, square sawn timbers; boiling treatment; longwise wood veneer slicer products, dried; classification and packaging. The surface smoothness of longwise wood veneer slicer at 3 different thickness levels from 1 mm, 2 mm, 3 mm was 87.36 µm; 88.10 µm; 80.99 µm respectively. The veneer thickness variation is within the allowable range of 0.05 mm to 0.06 mm; the tensile strength of veneer increased when increasing the veneer thickness.  The tensile strength of 1 to 3 mm thickness reaches 48.75 MPa to 53.52 Mpa, respectively. The quality of longwise wood veneer slicer from teak wood reached standard requirements and can be widely used as a covering material for the production of wooden furniture and construction components.

Tóm tắt

Phân tích, lựa chọn và đề xuất quy trình công nghệ tạo ván lạng dọc có chiều dày 1, 2, 3 mm từ gỗ Tếch bao gồm các giai đoạn chủ yếu: Lựa chọn nguyên liệu, xẻ tạo gỗ hộp; xử lý luộc gỗ làm dẻo; lạng dọc, sấy khô; phân loại và đóng gói. Xác định tính chất của ván lạng dọc ở 3 cấp chiều dày khác nhau từ 1, 2, 3 mm. Độ nhẵn bề mặt tương ứng với chiều dày ván lạng lần lượt là đạt giá trị từ 87,36 µm, 88,10 µm, 80,99 µm; sai số chiều dày ván lạng nằm trong khoảng cho phép 0,05 - 0,06 mm; độ bền kéo của ván lạng có xu hướng tăng khi tăng chiều dày ván lạng từ 1 - 3 mm tương ứng là 48,75 - 53,52 Mpa. Chất lượng ván lạng dọc từ gỗ Tếch đáp ứng yêu cầu đề ra có thể sử dụng rộng rãi làm vật liệu phủ mặt cho sản xuất đồ gỗ và các cấu kiện xây dựng.