NGHIÊN CỨU QUÁ TRÌNH TÁCH LOẠI LIGNIN GỖ MỠ CHO SẢN XUẤT CÁC VẬT LIỆU COMPOSITE TỔNG HỢP GỐC GỖ

Abstract

This paper presents a chemical modification of Manglietia glauca anet wood in two stages with sulfate agents (NaOH + Na₂S) and with (CH₃COOH+H₂O₂). Accordingly, the bleaching process consists of two stages: removing lignin by sulphate agent with the volume ratio NaOH: Na₂S: 3:1, treatment temperatura of 100^oC and treatment time of 3h. A lignin bleaching modification process were established with volume ratio H₂O₂: CH₃COOH: 2: 1, treatment temperatura of 100^oC and treatment time of 2h. The yield of wood obtained was 83.6%. The lignin removal efficiency was 38.2%. After the bleaching process, the wood sample became opaque white, the structure is flexible and easy to shape.

Tóm tắt

Bài báo trình bày quy luật tương tác của gỗ Mỡ dạng tấm với các tác nhân sunfat và hydrogen peroxit trong axit axetic với mục tiêu tách loại và biến tính tẩy trắng lignin mà vẫn giữ nguyên được cấu trúc dạng tấm phẳng của gỗ. Theo đó, quá trình biến tính tẩy trắng gồm hai công đoạn: xử lý tách loại lignin bằng tác nhân sunfat với tỷ lệ thể tích NaOH: Na₂S: 3: 1, ở nhiệt độ sôi của hỗn hợp, thời gian xử lý 3 giờ. Công đoạn xử lý bằng hỗn hợp H₂O₂: CH₃COOH với tỷ lệ thể tích là 2: 1 ở nhiệt độ sôi, trong vòng 2 giờ. Mẫu gỗ Mỡ sau đó được tẩy trắng hoàn toàn, hiệu suất gỗ thu được là 83,6%, hàm lượng lignin bị tách loại 38,2%, cấu trúc gỗ thông thoáng hơn, lộ rõ các bó xơ sợi, bề mặt được giải phóng tạo điều kiện cho quá trình tiếp xúc các hóa chất khác. Cấu trúc gỗ Mỡ thu được sau biến tính tẩy trắng mềm dẻo có khả năng uốn cong, thích hợp làm vật liệu composite tổng hợp gốc gỗ.